AZtec Reclassify Phase - 钢中的相鉴别

Steels are engineered with different microstructures for different applications. Austenite, ferrite, martensite and bainite are common phases in different steel alloys and the relative proportions of these different phases impact how the steel will behave in different regimes. For example, the amount of martensite will influence both strength and toughness. As a result, being able to measure the relative presence of these phases is important.

Electron back-scattering diffraction (EBSD) can readily separate austenite and ferrite due to a significant crystallographic difference between these two phases. In contrast, distinguishing martensite, bainite and ferrite is a challenge as the crystal structure of these three phases is essentially the same. All three have a body centred cubic (BCC) structure, with martensite and bainite being only slightly distorted from the ferrite BCC structure. This difference in crystal structure has presented challenges to researchers for many years.

By downloading this application note you will see:

  • A new and innovative method has been developed to discriminate phases based on EBSD pattern quality, with the solution being demonstrated on both ferritic-martensitic steel and TRIP steel samples
  • How the identification and quantification of these phases are important in understanding the steel performance and optimisation of steel design
点击下载应用报告
沪ICP备17031777号-1 公安机关备案号31010402003473